房管倫理重量計算公式

Formula for calculating ethical weight in housing management

4x壁厚 x(邊長-壁厚)x7.85

4x wall thickness x (edge length wall thickness) x7.85

其中，邊長和壁厚都以毫米為單位，直接把數值代入上述公式，得出即為每米方管的重里，以克為單位。

Among them, the side length and wall thickness are both measured in millimeters. By directly substituting the values into the above formula, the weight per meter of square tube is obtained, measured in grams.

如 30 x30 x2.5毫米的方管，按上述公式即可算出其每米重量為:

For a 30 x30 x2.5 mm square tube, the weight per meter can be calculated using the above formula as follows:

4x2.5x(30-2.5)x7.85=275x7.85=2158.75克，即約 2.16 公斤

4x2.5x (30-2.5) x7.85=275x7.85=2158.75 grams, which is approximately 2.16 kilograms

當壁厚和邊長都以毫米為單位時，4x壁厚x(邊長-壁厚)算出的是每米長度方管的體積 ，以立方厘米為單位，再乘以鐵的比重每立方厘米 7.85 克，得出即為每米方管以克為單位的重里。

When the wall thickness and side length are both measured in millimeters, 4x wall thickness x (side length wall thickness) is calculated as the volume of a square tube per meter length, measured in cubic centimeters. This is then multiplied by the specific gravity of iron, which is 7.85 grams per cubic centimeter, to obtain the weight in grams per meter of square tube.

房管有縫管和無縫管的鑒定方法

Identification methods for jointed and seamless pipes in building management

有縫管和無縫管的鑒定方法主要有觀察焊縫、硝酸酒精腐蝕、檢查內壁、壓力測試、化學成分分析等。

The identification methods for welded and seamless pipes mainly include observing the weld seam, nitric acid alcohol corrosion, inspecting the inner wall, pressure testing, chemical composition analysis, etc.

觀察焊縫

Observe the weld seam

有縫管的外表面通常會有明顯的焊縫，而無縫管的外表面沒有焊縫。可以通過目視檢查或觸摸來判斷是否存在焊縫。

The outer surface of welded pipes usually has obvious welds, while the outer surface of seamless pipes does not have welds. It can be determined whether there is a weld seam through visual inspection or touch.

硝酸酒精腐蝕

Nitric acid alcohol corrosion

使用新配制的硝酸酒精對鋼管表面進行腐蝕，有縫管會在焊縫處顯示出一條白色的細線，而無縫管則不會出現這樣的痕跡。

Using newly formulated nitric acid alcohol to corrode the surface of steel pipes, a white thin line will appear at the weld seam of welded pipes, while seamless pipes will not show such traces.

檢查內壁

Check the inner wall

有縫管的內壁通常會有焊筋，而無縫管的內壁沒有焊筋。可以通過觀察管子的內壁來判斷是否存在焊筋。

The inner wall of a welded pipe usually has welding ribs, while the inner wall of a seamless pipe does not have welding ribs. The presence of welding bars can be determined by observing the inner wall of the pipe.

壓力測試

Stress testing

有縫管能夠承受的最大使用壓力通常在20公斤以內，而無縫管可以承受更高的壓力。可以通過進行壓力測試來判斷鋼管的類型。

The maximum operating pressure that seamless pipes can withstand is usually within 20 kilograms, while seamless pipes can withstand even higher pressures. The type of steel pipe can be determined by conducting a pressure test.

化學成分分析

chemical composition

有縫管和無縫管的化學成分有所不同。生產無縫管的鋼材成分僅僅是達到ASTM的基本要求，而生產有縫管的鋼材則含有適用于焊接的化學成分。可以通過進行化學成分分析來判斷鋼管的類型。

The chemical composition of seamless and seamless pipes is different. The composition of steel used for producing seamless pipes only meets the basic requirements of ASTM, while steel used for producing welded pipes contains chemical compositions suitable for welding. The type of steel pipe can be determined by conducting chemical composition analysis.

綜上所述，通過上述方法可以有效地鑒定鋼管是無縫管還是有縫管。在實際操作中，可以根據具體情況選擇合適的方法進行鑒定

In summary, the above methods can effectively identify whether steel pipes are seamless or seamless. In practical operation, appropriate methods can be selected for identification based on specific circumstances

本文由濟南方管友情奉獻.更多有關的知識請點擊:http://www.liondatech.com我們將會對您提出的疑問進行詳細的解答，歡迎您登錄網站留言.

This article is a friendly contribution from Jinan Fangzheng For more information, please click: http://www.liondatech.com We will provide detailed answers to your questions. You are welcome to log in to our website and leave a message